Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | |
Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62-1 |
Viscosity | 18 cP @Load 5.00 kg, Temperature 220 °C | 18 cP @Load 11.0 lb, Temperature 428 °F | MVR cc/10 min; ISO 1133 |
Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 19.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 19.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 |
60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 | |
Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
Elongation at Break | 115 % | 115 % | 50 mm/min; ISO 527 |
117 % | 117 % | 50 mm/min; ASTM D638 | |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.32 GPa | 336 ksi | 50 mm/min; ASTM D638 |
2.45 GPa | 355 ksi | 1 mm/min; ISO 527 | |
Flexural Strength | 71.0 MPa | 10300 psi | yield, 2 mm/min; ISO 178 |
96.0 MPa | 13900 psi | yld, 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 2.31 GPa | 335 ksi | 2 mm/min; ISO 178 |
2.36 GPa | 342 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact Notched | 828 J | 611 ft-lb | ASTM D256 |
242 J @Temperature -30.0 °C | 178 ft-lb @Temperature -22.0 °F | ASTM D256 | |
Izod Impact, Notched (ISO) | 65.0 kJ/m? | 30.9 ft-lb/in? | 80*10*3; ISO 180/1A |
11.0 kJ/m? @Temperature -30.0 °C | 5.23 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 6.50 J/cm? | 30.9 ft-lb/in? | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
1.20 J/cm? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
Dart Drop, Total Energy | 72.0 J | 53.1 ft-lb | ASTM D3763 |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
CTE, linear, Transverse to Flow | 60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ASTM E831 |
60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C | 33.3 ?in/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
128 °C @Thickness 3.20 mm | 262 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
129 °C @Thickness 6.40 mm | 264 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
Vicat Softening Point | 140 °C | 284 °F | Rate B/120; ISO 306 |
141 °C | 286 °F | Rate B/50; ISO 306 | |
141 °C | 286 °F | Rate B/50; ASTM D1525 | |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
Zone 2 | 280 - 305 °C | 536 - 581 °F | |
Zone 3 | 295 - 315 °C | 563 - 599 °F | |
Melt Temperature | 295 - 315 °C | 563 - 599 °F | Injection Molding |
Mold Temperature | 70.0 - 95.0 °C | 158 - 203 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
48.0 hour | 48.0 hour | Cumulative; Injection Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
本公司长期销售沙伯基础 PC,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!
企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
---|---|---|---|
成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售:塑胶原料、化工原料(不含危险化学品)。 |