Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
Density | 1.20 g/cc | 0.0434 lb/in? | ISO 1183 |
Water Absorption | 0.35 % | 0.35 % | 23°C/sat; ISO 62 |
Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC method |
0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC method | |
Melt Flow | 21 g/10 min @Load 1.20 kg, Temperature 300 °C | 21 g/10 min @Load 2.65 lb, Temperature 572 °F | cm?/10 min; ISO 1133 |
22 g/10 min @Load 1.20 kg, Temperature 300 °C | 22 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell R | 120 | 120 | ASTM D785 |
120 | 120 | ISO 2039-2 | |
Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
63.0 MPa | 9140 psi | 50 mm/min; ASTM D638 | |
Elongation at Break | >= 70 % | >= 70 % | 50mm/min; ASTM D638 |
>= 70 % | >= 70 % | 50mm/min; ISO 527 | |
Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.35 GPa | 341 ksi | 1mm/min; ISO 527 |
2.35 GPa | 341 ksi | 50 mm/min; ASTM D638 | |
Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
Izod Impact, Unnotched | NB | NB | ASTM D4812 |
Izod Impact, Notched (ISO) | 65.0 kJ/m? | 30.9 ft-lb/in? | 80*10*3; ISO 180/1A |
12.0 kJ/m? @Temperature -30.0 °C | 5.71 ft-lb/in? @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
Dart Drop, Total Energy | 55.0 J | 40.6 ft-lb | peak; ASTM D3763 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
>= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
Dielectric Constant | 3.0 @Frequency 60.0 Hz | 3.0 @Frequency 60.0 Hz | ASTM D150 |
3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | IEC 60250 | |
3.0 @Frequency 60.0 Hz | 3.0 @Frequency 60.0 Hz | IEC 60250 | |
3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | ASTM D150 | |
Dielectric Strength | 27.0 kV/mm @Thickness 1.60 mm | 686 kV/in @Thickness 0.0630 in | ASTM D149 |
27.0 kV/mm @Thickness 1.60 mm | 686 kV/in @Thickness 0.0630 in | IEC 60243-1 | |
Dissipation Factor | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 |
0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 70.0 ?m/m-°C @Temperature -40.0 - 95.0 °C | 38.9 ?in/in-°F @Temperature -40.0 - 203 °F | ASTM E831 |
70.0 ?m/m-°C @Temperature 23.0 - 80.0 °C | 38.9 ?in/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ASTM C177 |
0.200 W/m-K | 1.39 BTU-in/hr-ft?-°F | ISO 8302 | |
Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60695-10-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
133 °C @Thickness 3.20 mm | 271 °F @Thickness 0.126 in | ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
122 °C @Thickness 3.20 mm | 252 °F @Thickness 0.126 in | ASTM D648 | |
Vicat Softening Point | 140 °C | 284 °F | Rate B/50; ISO 306 |
140 °C | 284 °F | Rate B/50; ASTM D1525 | |
Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | UL 94 |
Optical Properties | Metric | English | Comments |
Refractive Index | 1.586 | 1.586 | ISO 489 |
1.586 | 1.586 | ASTM D542 | |
Haze | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D1003 |
Transmission, Visible | 88 - 90 % @Thickness 2.54 mm | 88 - 90 % @Thickness 0.100 in | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Hopper Temperature |
Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
Zone 1 | 260 - 280 °C | 500 - 536 °F | |
Zone 2 | 270 - 290 °C | 518 - 554 °F | |
Zone 3 | 280 - 300 °C | 536 - 572 °F | |
Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
Moisture Content | 0.020 % | 0.020 % |
本公司长期销售沙伯基础 PC,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PEI料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!
企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
---|---|---|---|
成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售:塑胶原料、化工原料(不含危险化学品)。 |