Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
Water Absorption | 0.21 % @Time 86400 sec | 0.21 % @Time 24.0 hour | ASTM D570 |
Moisture Absorption | 0.0200 % | 0.0200 % | Injection Molding |
Water Absorption at Saturation | 1.2 % | 1.2 % | ASTM D570 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0060 in/in @Thickness 0.126 in | SABIC method |
Melt Flow | 7.0 g/10 min @Load 6.60 kg, Temperature 337 °C | 7.0 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 114 | 114 | ASTM D785 |
Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ASTM D638 |
Tensile Strength, Yield | 114 MPa | 16500 psi | 5 mm/min; ASTM D638 |
Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ASTM D638 |
Tensile Modulus | 4.68 GPa | 679 ksi | 5 mm/min; ASTM D638 |
Flexural Strength | 199 MPa | 28900 psi | brk, 2.6 mm/min, 100 mm span; ASTM D790 |
Flexural Modulus | 5.17 GPa | 750 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
Izod Impact Notched | 53.0 J | 39.1 ft-lb | ASTM D256 |
459 J @Thickness 3.20 mm | 339 ft-lb @Thickness 0.126 in | reverse notched; ASTM D256 | |
Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
Dielectric Constant | 3.5 @Frequency 1000 Hz | 3.5 @Frequency 1000 Hz | ASTM D150 |
Dielectric Strength | 27.6 kV/mm @Thickness 1.60 mm | 701 kV/in @Thickness 0.0630 in | in oil; ASTM D149 |
Dissipation Factor | 0.0014 @Frequency 1000 Hz | 0.0014 @Frequency 1000 Hz | ASTM D150 |
0.0046 @Frequency 2.45e+9 Hz | 0.0046 @Frequency 2.45e+9 Hz | ASTM D150 | |
Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
Hot Wire Ignition, HWI | 30 - 60 sec @Thickness >=1.50 mm | 30 - 60 sec @Thickness >=0.0591 in | UL 746A |
60 - 120 sec @Thickness >=3.00 mm | 60 - 120 sec @Thickness >=0.118 in | UL 746A | |
High Amp Arc Ignition, HAI | 0.00 - 15 arcs @Thickness >=3.00 mm | 0.00 - 15 arcs @Thickness >=0.118 in | UL 746A |
15 - 30 arcs @Thickness >=1.50 mm | 15 - 30 arcs @Thickness >=0.0591 in | UL 746A | |
High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 32.4 ?m/m-°C @Temperature -20.0 - 150 °C | 18.0 ?in/in-°F @Temperature -4.00 - 302 °F | ASTM E831 |
Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm | 410 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 208 °C @Thickness 6.40 mm | 406 °F @Thickness 0.252 in | unannealed; ASTM D648 |
Vicat Softening Point | 223 °C | 433 °F | Rate B/50; ASTM D1525 |
UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
Flammability, UL94 | V-0 @Thickness >=0.410 mm | V-0 @Thickness >=0.0161 in | UL 94 |
5VA @Thickness >=1.90 mm | 5VA @Thickness >=0.0748 in | UL 94 | |
Smoke Density | 1.8 | 1.8 | Flaming, Ds 4 min; ASTM E662 |
Oxygen Index | 47 % | 47 % | ASTM D2863 |
Processing Properties | Metric | English | Comments |
Nozzle Temperature | 345 - 400 °C | 653 - 752 °F | |
Zone 2 | 340 - 400 °C | 644 - 752 °F | |
Zone 3 | 345 - 400 °C | 653 - 752 °F | |
Melt Temperature | 350 - 400 °C | 662 - 752 °F | Injection Molding |
Mold Temperature | 135 - 165 °C | 275 - 329 °F | |
Drying Temperature | 150 °C | 302 °F | Injection Molding |
Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
24.0 hour | 24.0 hour | Cumulative; Injection Molding | |
Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |
Shot Size | 40 - 60 % | 40 - 60 % | |
Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
本公司长期销售沙伯基础 PEI,ABS,ASA,EVA,PA6,PBT,PE,PBT,PET,PMMA,POM,PS,PP,PU,PES,PC料等多种牌号
我司产品均可提供详细物性表(英文和中文版)相关资料;可开13%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、竭诚为您服务!
企业类型 | 个体工商户 | 统一社会信用代码 | 92441900MA51262745 |
---|---|---|---|
成立日期 | 2017-11-23 | 法定代表人/负责人 | 余成义 |
注册地址 | 东莞市樟木头镇樟罗龙腾花园一期16号铺位 | 营业期限 | 2017-11-23 至 无固定期限 |
登记机关 | 东莞市市场监督管理局 | 经营范围 | 销售:塑胶原料、化工原料(不含危险化学品)。 |