PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
MECHANICAL | ||||
Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 | |
Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 | |
Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 | |
Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 | |
IMPACT | ||||
Instrumented Dart Impact Total Energy, 23掳C | 33 | J | ASTM D3763 | |
Izod Impact, unnotched 80*10*4 +23掳C | NB | kJ/m虏 | ISO 180/1U | |
Izod Impact, unnotched 80*10*4 -30掳C | NB | kJ/m虏 | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23掳C | 5 | kJ/m虏 | ISO 180/1A | |
Izod Impact, notched 80*10*4 -30掳C | 5 | kJ/m虏 | ISO 180/1A | |
Charpy 23掳C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m虏 | ISO 179/1eA | |
THERMAL | ||||
CTE, 23掳C to 150掳C, flow | 5.E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 150掳C, xflow | 5.E-05 | 1/掳C | ISO 11359-2 | |
Vicat Softening Temp, Rate A/50 | 215 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/50 | 211 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 212 | 掳C | ISO 306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 200 | 掳C | ISO 75/Be | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | 掳C | ISO 75/Ae | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 193 | 掳C | ISO 75/Af | |
Metallized Haze Onset | 204 | 掳C | SABIC method | |
PHYSICAL | ||||
Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
Mold Shrinkage, xflow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
Density | 1.27 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/saturated) | 1.25 | % | ISO 62-1 | |
Moisture Absorption (23掳C / 50% RH) | 0.7 | % | ISO 62 | |
Melt Volume Rate, MVR at 360掳C/5.0 kg | 25 | cm鲁/10 min | ISO 1133 | |
Melt Flow Rate, 337掳C/6.7 kgf | 17.8 | g/10 min | ASTM D1238 | |
FLAME CHARACTERISTICS | ||||
FMVSS Burning Speed, thickness 2 mm | 0-5 | mm/min | FMVSS 302 | |
INJECTION MOLDING | ||||
Drying Temperature | 150 | 掳C | ||
Drying Time | 4-6 | Hrs | ||
Drying Time (Cumulative) | 24 | Hrs | ||
Maximum Moisture Content | 0.02 | % | ||
Melt Temperature | 350-400 | 掳C | ||
Nozzle Temperature | 345-400 | 掳C | ||
Front - Zone 3 Temperature | 345-400 | 掳C | ||
Middle - Zone 2 Temperature | 340-400 | 掳C | ||
Rear - Zone 1 Temperature | 330-400 | 掳C | ||
Mold Temperature | 135-165 | 掳C | ||
Back Pressure | 0.3-0.7 | MPa | ||
Screw Speed | 40-70 | rpm | ||
Shot to Cylinder Size | 40-60 | % | ||
Vent Depth | 0.025-0.076 | mm |
企业类型 | 有限责任公司(自然人独资) | 统一社会信用代码 | 91441900MA4UNCL112 |
---|---|---|---|
成立日期 | 2016-04-07 | 法定代表人/负责人 | 吴双发 |
注册资本 | 50万(元) | 注册地址 | 东莞市樟木头镇先威大道85-1号塑胶商务中心二期9栋32号 |
营业期限 | 2016-04-07 至 无固定期限 | 登记机关 | 东莞市市场监督管理局 |
经营范围 | 销售:塑胶原料、其他化工产品(不含危险化学品)、高分子材料。(依法须经批准的项目,经相关部门批准后方可开展经营活动)〓 |